تفاصيل الوثيقة نوع الوثيقة : مقال في مجلة دورية  عنوان الوثيقة : Fabrication of magnesium hydroxide nanoneedles Fabrication of magnesium hydroxide nanoneedles   الموضوع : كيمياء  لغة الوثيقة : الانجليزية  المستخلص : Magnesium hydroxide Mg(OH)2 nanoneedles with diameters of 40-60 nm and lengths of more than 650 nm have been fabricated by a fast and safe route in de-ionized water. X-ray diffraction (XRD) showed that the Mg(OH)2 nanoneedles were well-crystallized with the hexagonal structure, whereas from the morphological investigations using scanning electron microscope (SEM), it was revealed that the nanoneedles are grown in a very high density over the whole foil substrate. The structure features were also analyzed by high~resolution transmission electron microscopy (TEM). The approach is based on a simple reaction of magnesium foil and de-ionized water without using surfactants. The reaction time is 3 h and the temperature is ~110°C. The advantages of producing nanoneedles using this method include ease, flexibility, speed, and cost. The process can easily be scaled up.  ردمد : 0009-3092  اسم الدورية : Chemistry and Technology of Fuels and Oils  المجلد : 47  العدد : 2  سنة النشر : 1432 هـ 2011 م  نوع المقالة : مقالة علمية  تاريخ الاضافة على الموقع : Saturday, February 11, 2012  الباحثون اسم الباحث (عربي) اسم الباحث (انجليزي) نوع الباحث المرتبة العلمية البريد الالكتروني Ahmad A Al-Owais Al-Owais, Ahmad A باحث دكتوراه aowais21@yahoo.com السيد حسيني المسلمي El-Mossalamy, El-sayed H باحث دكتوراه sbdmina@yahoo.com محمد أشرف شاه Shah, Mohammad Ashraf باحث دكتوراه shahkau@hotmail.com H M Arafa Arafa, H M باحث دكتوراه han.m.a.2008@hotmail.com الملفات اسم الملف النوع الوصف  32230.pdf pdf Abstract الرجوع إلى صفحة الأبحاث