Optical characterization of nanocrystalline Se85 Te10 Pb5 and Se80 Te10 Pb10 chalcogenides
Optical characterization of nanocrystalline Se85 Te10 Pb5 and Se80 Te10 Pb10 chalcogenides
 
الموضوع : فيزياء 
لغة الوثيقة : الانجليزية 
المستخلص : Measurements of optical constants have been made on alloyed samples of Se and Te with Pb prepared under vacuum by diffusion methods. The polycrystalline Se85Te10Pb5 and Se80Te10Pb10 chalcogenides were used as a starting material for the milling process. The milled materials were characterized by TEM and optical measurements in a wavelength region of 400-1000 nm. The experimental result shows that the optical absorption follows the rules of direct transition. TEM measurements showed that after 60 h of milling, nanoparticles with a typical diameter of about 5 to 20 nm were developed. The optical band gap and optical constants of the milled materials in thin film form have been studied as a function of photon energy. It has been observed that the absorption coefficient, optical band gap and extinction coefficient increases while the refractive index decreases with an increase in milling time. The results have been analyzed on the basis of milling time. 
ردمد : 0749-6036 
اسم الدورية : Superlattices and Microstructures 
المجلد : 47 
العدد : 6 
سنة النشر : 1431 هـ
2010 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Monday, November 14, 2011 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
شمشاد أحمد خانKhan, Shamshad Ahmedباحثدكتوراهshamshad_phys@yahoo.com
فيصل عبدالعزيز العقلAl-Agel, Faisal Aباحثدكتوراهfagel@kau.edu.sa
أحمد عبدالله الغامديAl-Ghamdi, Ahmad AباحثدكتوراهAGAMDI@kau.edu.sa

الملفات

اسم الملفالنوعالوصف
 31244.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث