Kinetics of non-isothermal crystallization in Ga10Se90 chalcogenide glass
Kinetics of non-isothermal crystallization in Ga10Se90 chalcogenide glass
 
الموضوع : فيزياء 
لغة الوثيقة : الانجليزية 
المستخلص : The present research work deals with the thermal behavior of Ga10Se90 chalcogenide glass prepared by melt quenching technique. The kinetics of crystallization of Ga10Se90 glassy alloy at different heating rates 5, 10, 15, 20, 25, 30 K/min was studied by differential scanning calorimetry (DSC) using non-isothermal means. DSC experimental method is currently employed for determining the kinetic parameters of crystallization in Ga10Se90 glassy alloy. These parameters include the activation energy of crystallization (Ec), activation energy of glass transition temperature (Eg) and crystallization enthalpy (ΔHc). The average value of Ec is found to 96.06 kJ/mol and Eg is found to be 151.17 kJ/mol respectively. The results of crystallization have been discussed on the basis of different models such as Kissinger's approach and modification for non-isothermal crystallization in addition to Ozawa and Avrami. 
ردمد : 1584-8663 
اسم الدورية : Chalcogenide Letters 
المجلد : 7 
العدد : 9 
سنة النشر : 1431 هـ
2010 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Sunday, October 30, 2011 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
فيصل عبدالعزيز العقلAl-Agel, Faisal Aباحثدكتوراهfagel2@hotmail.com

الملفات

اسم الملفالنوعالوصف
 31203.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث