Kinetics of non-isothermal crystallization of ternary Se80Te20-xZnx glasses
Kinetics of non-isothermal crystallization of ternary Se80Te20-xZnx glasses
 
الموضوع : فيزياء 
لغة الوثيقة : الانجليزية 
المستخلص : The crystallization kinetics of Se80Te20-xZnx with x = 0.5, 1.0, 1.5, 2.0 and 2.5 chalcogenide glasses were investigated using non-isothermal crystallization approach. The glass transition temperature (Tg) and crystallization temperature (Tc) of these glasses were determined using the differential scanning calorimeter at different heating rates. The dependence of Tg and Tc on the heating rate (β) has been used for the determination of the activation energy of crystallization (Ec), the activation energy of structural relaxation (Et), crystallization enthalpy (ΔHc) and the Avrami exponent (n). It was found that the enthalpy released is minimum at 2.5% of Zn, hence, the glass with 2.5% of Zn is most stable in the Se80Te20-xZnx system. The crystallization kinetics for the glasses was studied by using the modified Kissinger and Ozawa equations. 
ردمد : 0925-8388 
اسم الدورية : Journal of Alloys and Compounds 
المجلد : 497 
العدد : 1 
سنة النشر : 1431 هـ
2010 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Tuesday, October 11, 2011 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
Anis AhmadAhmad, Anis باحثدكتوراه 
شمشاد أحمد خانKhan, Shamshad Ahmedباحثدكتوراهshamshad_phys@yahoo.com
أحمد عبدالله الغامديAl-Ghamdi, A AباحثدكتوراهAGAMDI@kau.edu.sa
فيصل عبدالعزيز العقلAl-Agel, Faisal Aباحثدكتوراهfagel@kau.edu.sa
Kirti SinhaSinha, Kirti باحثدكتوراه 
Mohd ZulfequarZulfequar, Mohd باحثدكتوراه 
M HusainHusain, M باحثدكتوراه 

الملفات

اسم الملفالنوعالوصف
 31008.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث